Two-component structural epoxy for bonding carbon fiber plates to concrete and steel.
Two-component, high-modulus epoxy paste adhesive for bonding pultruded CFRP plates to concrete, masonry, and steel substrates. Thixotropic consistency holds position on vertical and overhead surfaces without sagging. High elastic modulus (4.0 GPa) ensures efficient shear transfer between the plate and the structural substrate. Solvent-free, low VOC, moisture tolerant, and colour-coded for reliable mixing.
| Property | Value |
|---|---|
| Appearance | A: grey; B: white; Mixed: light grey |
| Mix Ratio | A:B = 2:1 by weight |
| Packaging | 10 kg (A) + 5 kg (B) per kit |
| Pot Life | 150 min (10°C) / 50 min (23°C) / 40 min (30°C) |
| Full Cure | 7 days (23°C) |
| Service Temperature | +5°C to +40°C |
| Thixotropic Index | ≥ 4.0 |
| Sagging | ≤ 2.0 mm |
| Consumption | 3–4 kg/m² |
| Tensile Strength | 45 MPa |
| Tensile Elastic Modulus | 4,000 MPa (4.0 GPa) |
| Elongation at Break | 2.07% |
| Compressive Strength | 117 MPa |
| Flexural Strength | 115 MPa |
| Density | 1.4 g/cm³ |
| HDT | 65°C |
| Water Absorption | 0.06% |
| Shear Strength (ASTM D732) | 56 MPa |
| Bond to Concrete (ASTM C882) | 40 MPa |