High-performance unidirectional carbon fiber fabrics for structural wrapping and reinforcement applications.
High-performance, unidirectional PAN-based carbon fiber fabric for externally bonded structural strengthening. Designed to work with FSE-series epoxy systems (FSE 302 primer and FSE 322 saturating resin) to form a high-performance FRP composite, the FSC fabric delivers exceptional tensile strength up to 4,500 MPa and elastic modulus of 240 GPa. Ideal for upgrading the load-bearing capacity and ductility of concrete, masonry, and timber elements including beams, columns, slabs, walls, and seismic retrofitting applications.
| Property | Value |
|---|---|
| Fibre Type | Carbon fibre, PAN-based, Unidirectional (0°) |
| Available Weights | 200 / 230 / 300 / 600 g/m² |
| Available Grades | Grade A (High Strength, T700) / Grade C (Economy, T300) |
| Available Widths | 100 / 150 / 200 / 250 / 300 / 500 / 600 mm |
| Roll Length | 100 m (standard) |
| Testing Standard | ASTM D3039 (≥ 25 specimens); Design per ACI 440.2R |
| Model | Weight | Thickness | Tensile Strength | Elastic Modulus | Elongation |
|---|---|---|---|---|---|
| FSC200A | 200 g/m² | 0.111 mm | 4,500 MPa | 240 GPa | 1.8% |
| FSC200C | 200 g/m² | 0.111 mm | 3,500 MPa | 230 GPa | 1.7% |
| FSC230A | 230 g/m² | 0.128 mm | 4,500 MPa | 240 GPa | 1.8% |
| FSC230C | 230 g/m² | 0.128 mm | 3,500 MPa | 230 GPa | 1.7% |
| FSC300A | 300 g/m² | 0.167 mm | 4,500 MPa | 240 GPa | 1.8% |
| FSC300C | 300 g/m² | 0.167 mm | 3,500 MPa | 230 GPa | 1.7% |
| FSC600A | 600 g/m² | 0.333 mm | 4,400 MPa | 235 GPa | 1.8% |
| FSC600C | 600 g/m² | 0.333 mm | 3,500 MPa | 230 GPa | 1.7% |